CF10簡介
USA ASTM Special Alloy CF10，及該型號鋼材的基本信息、化學元素成分、機械性能、力學性能、熱處理溫度、同等型號參照表等。
基本信息：
| 分類 |
種類 |
型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| Steel Grades |
|
CF10 |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
化學成分信息(mass fraction)(wt.%) of the CF10：
| 元素名稱 |
含量比例值 |
|---|
| C |
0.04-0.10 |
| Si |
2 |
| Mn |
1.5 |
| P |
0.04 |
| S |
0.04 |
| Cr |
18.0-21.0 |
| Ni |
8.0-11.0 |
| Mo |
≤0.50 |
機械性能信息：
| 屈服強度Rp0.2（MPa） |
抗拉強度Rm（MPa） |
沖擊率 |
伸長率 |
斷面收縮率 |
熱處理狀態(tài) |
布氏硬度（HBW） |
|---|
| 857 (≥) |
594 (≥) |
34 |
24 |
32 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
114 |
物理性質(zhì)信息：
| 溫度 |
彈性模量 |
系數(shù) |
熱導(dǎo)率 |
比熱容量 |
比電阻率 |
密度 |
加權(quán)系數(shù) |
|---|
| 33 |
- |
- |
|
|
0.12 |
- |
|
| 154 |
524 |
- |
13.3 |
412 |
|
- |
|
| 264 |
- |
32 |
24.2 |
|
|
313 |
242 |
熱處理信息：
| 熱處理溫度區(qū)間 |
|---|
| Heat treated : 1391°C - 1947°C |
對照表（同等等級）信息：
| 型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| ASTM CF10 |
AISI |
USA |
|
| ASTM CF10M |
AISI |
USA |
|
| ASTM CF10MC |
AISI |
USA |
|
| ASTM CF10SMnN |
AISI |
USA |
|
| CF10 |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10M |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10MC |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10SMnN |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10 |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10M |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10MC |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |
| CF10SMnN |
ASTM |
USA |
Steel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application |